CRAYVALLAC SL
CRAYVALLAC? SL
Micronised Amide Wax Rheology Modifier
Product Benefits
CRAYVALLAC? SL is a high performance micronised amide wax rheology modifier designed for the high temperature manufacture of moisture curing methoxysilane based sealants.
CRAYVALLAC? SL is also suitable for the high temperature manufacture of moisture curing methoxysilane based adhesives.
CRAYVALLAC? SL is designed for use in one component methoxysilane sealants where in comparison to hydrogenated castor oil based products and fumed silica its key advantages are minimal effect on modulus and very good stability on storage.
With one component moisture curing methoxysilane based sealants,CRAYVALLAC? SL is generally added along with the initial charge of methoxysilane polymer and plasticiser to a vacuum dispersion vessel with heating capability. This is followed by the pigments and extenders. Efficient activation of CRAYVALLAC? SL is achieved during the vacuum dispersion stage by allowing the batch temperature to rise to 90 - 115°C (194 - 239°F). This condition of dispersion would typically be maintained for approximately 30 minutes at 110°C (230°F), or until the required level of dispersion is obtained and a suitably low moisture content has been achieved (typically < 800 p.p.m.). Following this, the batch temperature is lowered sufficiently to allow for the safe addition of such additives as moisture scavengers, adhesion promoters and reaction catalysts.
The activation process constitutes the conversion of the CRAYVALLAC? SL particles to an interacting network of crystalline fibres. It is this network that gives rise to the shear thinning rheology. This shear thinning characteristic provides for a low viscosity at the shear rates associated with application by extrusion, and a very high viscosity under the low shear rates experienced after application. The net result is ease of application followed by excellent sag and slump resistance.
Activation at too low a temperature, or for too short a time, will result in the formation of an inefficient interacting network and consequently poor sag and slump resistance.
The successful manufacture of methoxysilane based sealants is very dependent on the careful control of moisture levels throughout manufacture and storage. For this reason it is normal practice to pre-dry all pigments and extenders prior to dispersion with the methoxysilane polymer. Alternatively, special grades of low moisture content ingredients may be used.
The use of vacuum processing at elevated temperatures serves two key purposes;it prevents the take up of moisture during processing and facilitates the removal of any unwanted water residues introduced with the raw materials.
With moisture cured methoxysilane based sealants, we strongly recommend that all additives be quickly dispersed and not allowed to remain in direct contact with the resin component. Prolonged contact may sometimes result in the formation of an insoluble fine skin which later appears as small particles in the final sealant.
Performance Benefits
·100% active
·Efficient activation at 90 - 115°C (194 - 239°F)
·Imparts shear thinning rheology
·Very good extrusion properties
·Excellent sag and slump resistance
·Minimal effect on modulus
·Excellent storage stability
Recommendations for Use
For one component moisture curing methoxysilane based sealants, excellent slump and sag control will generally be obtained when CRAYVALLAC? SL is used at a level of 1 - 5% by mass on total formulation.
Sales Specifications
Particle size distribution:(Malvern Mastersizer S laser particle size analyser) (CR 005)
DV. 1 min. 1.8 μm
DV. 9 max. 15.0 μm
Other Properties
Density at 25°C (77°F), g/cm3 (CR006) 0.99
Bulk density, g/cm3 (CR016) 0.4-0.6
Appearance Off White Powder
Capillary Melting Point (CR003) 120-130°C(248-266°F)